{"paper":{"title":"Effect of mixed pinning landscapes produced by 6 MeV Oxygen irradiation on the resulting critical current densities J$_c$ in 1.3 $\\mu$m thick GdBa$_2$Cu$_3$O$_{7-d}$ coated conductors grown by co-evaporation","license":"http://arxiv.org/licenses/nonexclusive-distrib/1.0/","headline":"","cross_cats":[],"primary_cat":"cond-mat.supr-con","authors_text":"F. Golmar, H. Troiani, Jae-Hun Lee, N. Haberkorn, P. D. P\\'erez, P. Granell, S. H. Moon, S. Su\\'arez","submitted_at":"2017-06-13T19:09:22Z","abstract_excerpt":"We report the influence of crystalline defects introduced by 6 MeV $^{16}$O$^{3+}$ irradiation on the critical current densities J$_c$ and flux creep rates in 1.3 $\\mu$m thick GdBa$_2$Cu$_3$O$_{7-d}$ coated conductor produced by co-evaporation. Pristine films with pinning produced mainly by random nanoparticles with diameter close to 50 nm were irradiated with doses between 2x10$^{13}$ cm$^{-2}$ and 4x10$^{14}$ cm$^{-2}$. At temperatures below 40 K with the magnetic field applied parallel (H//c) and at 45{\\deg} (H//45{\\deg}) to the c-axis, the in-field J$_c$ dependences can be significantly im"},"claims":{"count":0,"items":[],"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"source":{"id":"1706.04228","kind":"arxiv","version":3},"verdict":{"id":null,"model_set":{},"created_at":null,"strongest_claim":"","one_line_summary":"","pipeline_version":null,"weakest_assumption":"","pith_extraction_headline":""},"references":{"count":0,"sample":[],"resolved_work":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57","internal_anchors":0},"formal_canon":{"evidence_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"author_claims":{"count":0,"strong_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"builder_version":"pith-number-builder-2026-05-17-v1"}