{"paper":{"title":"Fe-rich border of miscibility gap and activation energy of phase decomposition in a Fe-Cr alloy","license":"http://arxiv.org/licenses/nonexclusive-distrib/1.0/","headline":"","cross_cats":[],"primary_cat":"cond-mat.mtrl-sci","authors_text":"J. Zukrowski, S. M. Dubiel","submitted_at":"2012-04-18T08:01:00Z","abstract_excerpt":"Concentration of Cr in the Fe-rich alpha-phase, x, resulted from a phase decomposition caused by an isothermal annealing at T = 415 and 450 C of a non-irradiated (NR) Fe-Cr14 EFDA sample and that of a He-ions irradiated (IR) one annealed at 415 C was determined with M\\\"ossbauer spectroscopy. The x-value in the latter was by ~3 at% higher than the one in the NR-counterpart. The activation energy for the phase decomposition in the NR-sample was 122 kJ/mol. In the IR-sample its value was by 12 kJ/mol lower. Avrami exponents for the NR-samples were close to 0.5, and that for the IR-sample had a va"},"claims":{"count":0,"items":[],"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"source":{"id":"1204.4002","kind":"arxiv","version":2},"verdict":{"id":null,"model_set":{},"created_at":null,"strongest_claim":"","one_line_summary":"","pipeline_version":null,"weakest_assumption":"","pith_extraction_headline":""},"references":{"count":0,"sample":[],"resolved_work":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57","internal_anchors":0},"formal_canon":{"evidence_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"author_claims":{"count":0,"strong_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"builder_version":"pith-number-builder-2026-05-17-v1"}