{"paper":{"title":"Polycrystalline {\\gamma}-boron: As hard as polycrystalline cubic boron nitride","license":"http://arxiv.org/licenses/nonexclusive-distrib/1.0/","headline":"","cross_cats":[],"primary_cat":"cond-mat.mtrl-sci","authors_text":"Duanwei He, Hiroaki Ohfuji, Jiaqian Qin, Li Lei, Norimasa Nishiyama, Tetsuo Irifune, Toru Shinmei","submitted_at":"2012-03-08T10:58:46Z","abstract_excerpt":"The Vickers hardness of polycrystalline {\\gamma}-B was measured using a diamond indentation method. The elastic properties of polycrystalline {\\gamma}-B (B=213.9 GPa, G=227.2 GPa, and E=503.3 GPa) were determined using ultrasonic measurement at ambient condition. Under the loading force up to 20 N, our test gave an average Vickers hardness in the asymptotic-hardness region of 30.3 GPa. The average fracture toughness was measured as 4.1MPa m1/2. Additionally, We also measured the hardness and elastic properties of polycrystalline {\\beta}-B and PcBN for comparison. The hardness and elastic prope"},"claims":{"count":0,"items":[],"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"source":{"id":"1203.1748","kind":"arxiv","version":3},"verdict":{"id":null,"model_set":{},"created_at":null,"strongest_claim":"","one_line_summary":"","pipeline_version":null,"weakest_assumption":"","pith_extraction_headline":""},"references":{"count":0,"sample":[],"resolved_work":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57","internal_anchors":0},"formal_canon":{"evidence_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"author_claims":{"count":0,"strong_count":0,"snapshot_sha256":"258153158e38e3291e3d48162225fcdb2d5a3ed65a07baac614ab91432fd4f57"},"builder_version":"pith-number-builder-2026-05-17-v1"}