Experimental measurements on broad-area 1300 nm lasers show that a highly strained In0.74Ga0.26As/In0.53Al0.25Ga0.22As superlattice active region yields ~6 cm^{-1} internal loss, ~500 A/cm^{2} transparency current density, 46 cm^{-1} modal gain, 53% internal efficiency, and characteristic temps T0=