Large-area epitaxial Fe3GaTe2/graphene heterostructures grown by MBE exhibit above-room-temperature ferromagnetism with TC up to 400 K and robust PMA.
Lateral spin filter realized by monolayer Fe 3GaTe2 and Fe3GaTe2/Graphene van der Waals heterostructures
2 Pith papers cite this work. Polarity classification is still indexing.
2
Pith papers citing it
fields
cond-mat.mtrl-sci 2verdicts
UNVERDICTED 2representative citing papers
Ni doping in MBE-grown Fe3GeTe2 films shrinks the lattice, suppresses PMA, and reduces Curie temperature to 50 K via substitution and intercalation, supported by structural, magnetic, and DFT measurements.
citing papers explorer
-
Above-room-temperature ferromagnetism in large-area epitaxial Fe3GaTe2/graphene van der Waals heterostructures
Large-area epitaxial Fe3GaTe2/graphene heterostructures grown by MBE exhibit above-room-temperature ferromagnetism with TC up to 400 K and robust PMA.
-
Tuning Structure and Magnetism in Large-Scale 2D Ferromagnet Fe$_3$GeTe$_2$ through Ni Doping
Ni doping in MBE-grown Fe3GeTe2 films shrinks the lattice, suppresses PMA, and reduces Curie temperature to 50 K via substitution and intercalation, supported by structural, magnetic, and DFT measurements.