Thermal treatment of superconductor thin film of the BSCCO system using domestic microwave oven

In this work, we report the preparation of a superconductor thin film of the BSCCO system using a good quality powder with nominal composition Bi_{1.8}Pb_{0.4}Sr_2CaCu_2O_x which was thermally treated using a domestic microwave oven (2.45 GHz, 800 W). This film was grew on a single crystal of LaAlO_3(100) substrate and exhibited a crystalline structure with the c-axis perpendicular to the plane of the substrate. An onset superconducting transition temperature was measured at 80 K.