Structure, heat capacity and Raman spectra of mm-sized Ba₂MgWO₆ single crystals synthesized by BaCl₂-MgCl₂ flux method

We present a new method of Ba$_{2}$MgWO$_{6}$ single crystal synthesis that allows to grow larger crystals using BaCl$_{2}$ and MgCl$_{2}$ flux. Difficulties to grow single crystal of a size suitable for macroscopic material property measurements caused the majority of characterisation being published on polycrystalline samples. Single crystal diffraction and energy dispersive X-ray analysis confirmed high quality of synthesised samples. Heat capacity measurements from 300~K to 2~K do not show any transitions. However, Raman spectra measured down to 77~K contain additional peaks at all temperatures probed, which is in a contrast with only 4 Raman active modes expected from the reducible representation. This calls for a more detailed study of potential symmetry breaking that could also influence the electronic properties of the material.