Observation of high-temperature superconductivity in the high-pressure tetragonal phase of La2PrNi2O7-{\delta}

The recent discovery of high-temperature superconductivity in the Ruddlesden-Popper phase La3Ni2O7 under high pressure marks a significant breakthrough in the field of 3d transition-metal oxide superconductors. For an emerging novel class of high-Tc superconductors, it is crucial to find more analogous superconducting materials with a dedicated effort toward broadening the scope of nickelate superconductors. Here, we report on the observation of high-Tc superconductivity in the high-pressure tetragonal I4/mmm phase of La2PrNi2O7 above ~10 GPa, which is distinct from the reported orthorhombic Fmmm phase of La3Ni2O7 above 14 GPa. For La2PrNi2O7, the onset and the zero-resistance temperatures of superconductivity reach Tconset = 78.2 K and Tczero = 40 K at 15 GPa. This superconducting phase shares the samilar structural symmetry as many cuprate superconductors, providing a fresh platform to investigate underlying mechanisms of nickelate superconductors.