Grain boundary-assisted bulk dealloying below the parting limit occurs via diffusion-induced recrystallization that generates high-density GB networks enabling molten-salt infiltration.
King, Diffusion induced grain boundary migration, International Materials Reviews 32 (1987) 173–189
2 Pith papers cite this work. Polarity classification is still indexing.
2
Pith papers citing it
citation-role summary
background 1
citation-polarity summary
fields
cond-mat.mtrl-sci 2years
2026 2roles
background 1polarities
background 1representative citing papers
Diffusion-induced grain boundary migration is the dominant mechanism for rapid Cr dealloying and porosity formation in Ni-30Cr during molten chloride salt exposure, with surface-induced grain structure dictating the corrosion morphology.
citing papers explorer
-
Role of diffusion-induced grain boundary migration during molten salt corrosion of a Ni-30Cr alloy
Diffusion-induced grain boundary migration is the dominant mechanism for rapid Cr dealloying and porosity formation in Ni-30Cr during molten chloride salt exposure, with surface-induced grain structure dictating the corrosion morphology.