Doping effects on the valence bond solid of Li₂RuO₃ with Mn substitution

$Li_{2}RuO_{3}$ with a honeycomb structure undergoes a drastic transition from a regular honeycomb lattice with the $C2/m$ space group to a valence bond solid state of the $P2_{1}/m$ space group with an extremely strong dimerization at 550 K. We synthesized $Li_{2}Ru_{1-x}Mn_{x}O_{3}$ with a full solid solution and investigated doping effects on the valence bond solid state as a function of Mn content. The valence bond solid state is found to be stable up to $x = 0.2$, based on our extensive experiments: structural studies, resistivity, and magnetic susceptibility. On the other hand, the extended x-ray absorption fine structure analyses show that the dimer local structure remains robust even above $x = 0.2$ with a minimal effect on the dimer bond length. This indicates that the locally-disordered dimer structure survives well into the Mn-rich phase even though the thermodynamically stable average structure has the $C2/m$ space group. Our results prove that the dimer formation in $Li_{2}RuO_{3}$ is predominantly a local phenomenon driven by the formation of orbitally-assisted metal-metal bonds and that these dimers are relatively robust against doping-induced disorder.