Room Temperature Magneto-dielectric coupling in the CaMnO3 modified NBT lead-free ceramics

The sol-gel prepared (1-x) Na0.5Bi0.5TiO3- (x) CaMnO3 (x=0, 0.03, 0.06, 0.12) compositions show a Rhombohedral (R3c) phase for x=0.06 while a mixed Rhombohedral (R3c) and orthorhombic (Pnma) phases for the x=0.12. The lattice volume consistently decreased with an increase in the CaMnO3 content. The phase transition temperature (Tc) decreased with an increase in the CaMnO3 compositions. The room temperature dielectric constant increased, and loss decreased for the x=0.03 composition due to a decrease in the oxygen vacancy and Bi loss confirmed by the valence state study (XPS). All the compositions show a variation of the room temperature dielectric property with an application of magnetic field confirming a magnetodielectric coupling. The x=0.06 composition shows the highest negative magnetodielectric constant (MD%) of 3.69 at 100kHz at an applied field of 5 kG.