Defect-engineered BeN2 monolayers with alkali-metal decoration store up to 11.64 wt% H2 with reversible adsorption energies of -0.17 to -0.19 eV.
A first-principles study of Li and Na co-decorated T4,4,4-graphyne for hydrogen storage
2 Pith papers cite this work. Polarity classification is still indexing.
2
Pith papers citing it
citation-role summary
background 1
citation-polarity summary
fields
cond-mat.mtrl-sci 2years
2026 2verdicts
UNVERDICTED 2roles
background 1polarities
background 1representative citing papers
N-GDY with dispersed Li/Na/K/Ca dopants achieves 9.15-13.08 wt% intrinsic H2 capacity with reversible near-ambient adsorption per DFT, AIMD and Langmuir modeling.
citing papers explorer
-
Defect-Engineered Beryllium Dinitride (BeN2) Monolayer with Light-Metal Decoration for Reversible High-Capacity Hydrogen Storage
Defect-engineered BeN2 monolayers with alkali-metal decoration store up to 11.64 wt% H2 with reversible adsorption energies of -0.17 to -0.19 eV.
-
N-Graphdiyne as a Tunable Platform for Stabilizing Light Metals toward High-Capacity Reversible Hydrogen Storage
N-GDY with dispersed Li/Na/K/Ca dopants achieves 9.15-13.08 wt% intrinsic H2 capacity with reversible near-ambient adsorption per DFT, AIMD and Langmuir modeling.