AlN Gate Interlayer for UWBG AlGaN Transistors with Breakdown Field >6.9 MV/cm and PFOM >1.8 GW/cm2

We report the demonstration of regrown epitaxial AlN gate interlayers with ultra-wide bandgap (UWBG) AlGaN polarization-graded field effect transistors (PolFETs). The introduction of the epitaxial AlN gate interlayer enables significant improvement in breakdown strength, with average breakdown field exceeding 6.94 MV/cm, which represents state-of-the-art for lateral field effect transistors, while maintaining excellent on-state current density exceeding 1 A/mm. The integration of epitaxial AlN enables state-of-the-art power-switching figure of merit exceeding 1.87 GW/cm2 at a breakdown voltage exceeding 1.45 kV. This work shows the potential of UWBG AlGaN for next-generation high-power switching and RF applications with enhanced device performance established by a high-quality epitaxially regrown AlN gate interlayer.